Čimbenici koji utječu na silu sidrenja putničkih šiljaka i metoda za njihovo poboljšanje
- Koji su osnovni faktori koji utječu na silu sidrenja Spike?
The strength of anchoring materials is crucial. The compressive strength of sulfur anchoring agent must be ≥40MPa; if it is lower than 30MPa, the anchoring force will decrease by 30% - 40%. The water - cement ratio must be controlled within the range of 0.3 - 0.35. The fit gap between the nail hole diameter and the spike should be moderate. An excessively large gap (>3mm) će smanjiti silu sidrenja za 20%- 25%, dok pretjerano mali jaz (<1mm) makes it difficult for the anchoring agent to fill. The optimal gap is 1.5 - 2mm to ensure uniform wrapping force. Insufficient spike embedding depth (<100mm) will reduce the anchoring force by 40% - 50%. The standard embedding depth should be 120 - 150mm, and the embedded part must have threads or barbs to increase mechanical biting force. Insufficient pouring of anchoring agent (voids >5%) uzrokovati da se koncentracija lokalnog stres, a fluktuacija sidrene sile dostiže 15% - 20% . izlivanje pritiska mora se koristiti za osiguravanje kompaktnosti .
- Koje su razlike u silu sidrenja šiljaka između različitih sidrišta?
Sumporni agent za sidrenje: Sand=1: 0 . 3: 1 . 3: 1 . 3: 1 . 3: 1 . kn, sa brzom podešavanjem (30 minuta), ali je lako zaseda za 20% u ordinarnim železnicama . sidrenog agenta (epoksidna smola + Sredstvo za sušenje) ima sidrući silu od80 - 100 kn, sa dobrim vremenskim otpornošću . sila sila je manja od ili jednaka 10% u rasponu od . agenta i hladnih regija . cementni agent za sidrenje ima niže sidrenu sidru (40 - 60 kn) ali dobro Zaštita životne sredine, pogodna za urbana željeznička tranzita . 5% 膨胀剂 mora se dodati da nadoknadi skupljanje i izbjegavanje sidrene sile. Kada je čelični sadržaj vlakana 3% - 5%, čvrstoća smicanja povećava se za 25%- 30%, koristi se u ključnim presjecima teških željeznica.
- Kako proces izgradnje utječe na silu sidrenja Spike?
Incomplete cleaning of nail holes (residual dust >5%) će smanjiti silu za sidrenje za 15% - 20% . puške u tlaku, a žičane četke moraju se koristiti ako je potrebno kako bi se osigurala plutajuća šljaka na unutrašnjem zidu noktiju . preniska temperatura sidrenog agenta (<130℃ for sulfur anchoring) will lead to poor fluidity and incomplete filling, reducing the anchoring force by 25% - 30%. The pouring temperature must be controlled at 140 - 160℃. A deviation of spike insertion depth >5mm će učiniti distribuciju sidreće sile, a razlika sidrene sile u istoj seriji može se dostići 10% - 15% .) za pozicioniranje, za vrijeme umetanja kako bi se osigurala ujednačena dubina, s odstupanjem manjim ili jednakim do 3 mm. nesigurno vrijeme stvrdnjavanja (<24 hours) will make the anchoring agent strength not up to standard, and the anchoring force is only 70% - 80% of the design value. Resin anchoring agent needs to be cured for more than 48 hours, and sulfur anchoring agent needs to be naturally cooled to room temperature (≥6 hours).
- Kako faktori okoliša utječu na silu sidrenja Spike?
A humid environment will reduce the bonding force between the anchoring agent and the nail hole. When the relative humidity is >90%, the anchoring force decreases by 10% - 15%. Rainy day construction must take rainproof measures to ensure that the nail hole is dry (moisture content ≤5%). A high - temperature environment (≥35℃) will accelerate the curing of resin anchoring agent, and concentrated reaction heat release may cause internal cracking, with an anchoring force loss of 20% - 25%. Retarders must be added to the anchoring agent to extend the gel time to 30 - 40 minutes. Freeze - thaw cycles (- 20 - 20℃) will cause microcracks in the anchoring agent. After 200 cycles, the anchoring force decreases by 30% - 40%. Frost - resistant anchoring agent (adding air - entraining agent, air content 3% - 5%) must be selected in cold regions. Saline - alkaline soil will erode the anchoring agent. When the chloride ion concentration is >500mg / L, sila sidrenja priguševa za 5% - 8% . protiv korozije obložene šiljcima i alkali - otporni sredstvo za sidrenje mora se koristiti u obalnim područjima .
- Koje su specifične mjere za poboljšanje sile sidrenja Spike?
Optimizirajte formulu agenta za sidrenje: dodavanje 5% - 8% Grafitni prah za sredstvo za sidrenje sumpor može povećati silu sidrenja za 10% - 15% i poboljšati fluidnost; Dodavanje 1% - 2% SILANSKOG Agenta za sidrenje silama koji se povećava sučelje sa šiljcima . Pomoć za sidrenje: Povećavanje kosine za povećanje sidrene sile za 20% - 25% . teške - železničke šiljke moraju usvojiti Ova struktura . Poboljšavaju proces izgradnje: Pregrijavanje rupe za nokte (40 - 50 stepen) za poboljšanje fluidnosti sidrenog sredstva, posebno pogodno za zimsku konstrukciju: 10% šiljaka u običnim železnicama uzorkuje se svake 2 godine, a sićne sile niže od 80% vrednosti dizajna trebaju biti re. Sidra . Velike željeznice otkrivene su jednom godišnje kako bi se osiguralo da sila sidrenja ispunjava standard (veću ili jednaku ili jednaku od 60kn) .)